Marble Grain Coated Aluminum

 

The marble grain coated aluminum is high end color coated aluminum product with beautiful marble and stone look for used in decoration. The base material of marble grain coated aluminum sheet often adopts 1100 H24, 1060 H24, 3003 H24, 5005 H24 and other alloys.

marble grain coated aluminum

Production process of marble grain coated aluminum mainly includes the following steps:

Aluminum substrate coil: choose suitable aluminum coil as the substrate.

Pre-treatment: Pre-treatment of aluminum coil surface such as cleaning, drying and fine straightening.

Chemical Roller Coating: Paint is applied to the surface of aluminum coil by rubber or steel rollers, so that the paint is leveled and aligned.

Drying and curing: The coated aluminum coil is dried and cured at high temperature to form a stable coating.

Printed Texture Coating: Marble texture is printed on the coated surface and baked and cured again.

Varnish baking: Cover the textured coating with a layer of varnish for final baking and curing.

Protective film and packaging: Cold-coating the finished product with protective film, and carrying out inspection and qualified packaging.

Advantages of marble grain coated aluminum:

Corrosion resistance: after special coating treatment, marble grain aluminum sheet has excellent corrosion resistance, able to resist acid rain, air pollution and ultraviolet rays.

UV resistance: the coating can effectively resist the attack of ultraviolet rays and keep the color bright for a long time.

Fire resistance: Aluminum trim is made of high-strength aluminum alloy and fluorocarbon (PVDF) paint or panel, which has good fire resistance.

Self-cleaning: special molecular structure so that dust can not adhere to the surface, with good self-cleaning.

Machinability: good performance of processing technology, can be processed into flat plate, curved plate surface and spherical panel and other complex various geometric shapes.

Environmental protection: made of aluminum-magnesium alloy and other materials, green and environmentally friendly, and light weight, high strength, easy to recycle and reuse.

Marble grain coated aluminum are widely used in the field of architectural decoration, including the decoration of the exterior walls of high-grade residences, commercial buildings, hotels, office buildings and other buildings. Meanwhile, it is also used for interior decoration, such as ceiling, wall, doors and windows. In addition, it can be used in the production of display cabinets, furniture, etc. to increase the texture and aesthetics of products. Its unique texture and color present an original design effect, which is suitable for the decorative needs of various high-grade places.

This resource is from https://www.aluminum-coil.net/marble-grain-coated-aluminum.html
Should you be interested in, please contact us at:
Haomei Aluminum
Whatsapp/Wechat: 0086 181 3788 9531
Email: nydia@aluminumhm.com

评论

发表评论

此博客中的热门博文

Differences between PS and CTP base plate

图片
With the increasing maturity and the rapid development of CTP technology, as well as the declining of price, CTP technology has been more and more welcomed by the majority of printing practitioners, usage of CTP plates have the potential trend to catch up with the traditional PS plate. The overall requirements of the printing plate is very high, especially the current CTP plate is mostly used for high-grade color printing plate, to ensure the quality of the plate, the plate based apparent quality is the premise. The characteristic of CTP technology is the quality of CTP based plate, such as the apparent quality, physical property and electrolytic performance. The aluminum plate base is widely used according to CTP plate technical requirement. The difference between CTP plates and PS plate on the apparent properties of aluminum plate base are as follows. The basic appearance requirements of the aluminum base plate is clean and smooth, no cracks, corrosion pits, air vents, scratches,...
阅读全文

Mill Finish Aluminum Foil 8011 H14 For Bottle Caps

图片
  Mill finish aluminum foil 8011 H14 for bottle caps has good performance and wide range of applications, usually used to make wine and cosmetic bottle caps. 8011 H14 mill finish aluminum foil for bottle cap material is mainly made of 8011 aluminum alloy, with good corrosion resistance and machinability. H14 temper refers to the hardness state of 8011 aluminum alloy after processing, aluminium foil 8011 h14 has a certain degree of hardness and strength. Mill finish means that the surface of aluminum foil is polished to give it a smooth surface and increase the aesthetic appearance. Mill finish 8011 H14 aluminum foil for bottle cap material has good sealing and freshness preservation properties, and is suitable for all kinds of bottle caps. In the production process, mill finish aluminum foil 8011 H14 for bottle caps material is completed through a number of processes such as cold rolling, foil rolling annealed thickness, annealing, foil rolling finished product, bending and st...
阅读全文

Introduction of aluminum foil insulation material

图片
Aluminum foil insulation material is the best thermal insulation material at present in the world. It has the advantages of light weight, low thermal conductivity, good heat resistance, aging resistance, easy combustion with other substrates, bonding does not produce droplet and other excellent properties. On the application, it is widely used in building roofing, wall, ceiling, floor, doors and windows as insulation materials. Aluminum foil itself is a good conductor of heat, directly used basically has no heat insulation, but accelerate the heat loss, so when used the insulation cotton is wrapped inside the aluminum foil . It has the functions of heat insulation, waterproof, moisture-proof and so on. Its solar radiation absorption coefficient is very low, which can insulate most of the heat transfer. Introduction of advantages of aluminum foil insulation material: (1) Simplification of structure to avoid waste. (2) It is unnecessary to set roof exhaust system. (3) Waterproof lay...
阅读全文