5052 aluminum sheet factory China

In China, you can find a professional 5052 aluminum sheet factory, Haomei Aluminum have about 20 years experience on aluminum sheet plate product manufacturing. 5052 aluminum sheet is a commonly used aluminum-magnesium alloy plate. Its main component is magnesium, and a small amount of manganese, chromium, titanium and other elements are added. The main impurity elements are iron, silicon, copper, zinc and so on. 5052 aluminum sheet factory The influence of magnesium and manganese on the properties of 5052 aluminum sheet are: 

(1) Magnesium 

Magnesium mainly exists in a solid solution state and β (Mg2Al3 or Mgs Al) phase. Although the solubility of magnesium in the alloy decreases rapidly with the decrease of temperature, it is difficult to precipitate and nucleate, and there are few cores and coarse precipitates. Therefore, the aging strengthening effect of the alloy is low, and it is generally used in an annealed or cold worked state. Therefore, this series of alloys is also called non-strengthetable aluminum; alloy. The strength of this series of alloys increases with the increase of magnesium content, while the plasticity decreases accordingly, and its processing performance also deteriorates. Magnesium content has a great influence on the recrystallization temperature of the alloy. When w(Mg)<5%, the recrystallization temperature decreases with the increase of magnesium content. When w(Mg)>5%, the recrystallization temperature changes with the magnesium content. Increase and increase. Magnesium content also has a significant effect on the welding performance of the alloy. When w(Mg)<6%, the welding crack of the alloy; the tendency of grains to decrease with the increase of magnesium content, when w(Mg)>6%, the opposite is true; When (Mg)<9%, the strength of the weld increases significantly with the increase of magnesium content. At this time, although the plasticity and welding coefficient gradually decrease slightly, the change is not large. When w(Mg)>9%, its The strength, plasticity and welding coefficient are all significantly reduced. 

(2) Manganese 

In the 5052 aluminum sheet alloy, usually w(Mn)<1.0%. Part of the manganese in the alloy is dissolved in the matrix, and the rest exists in the structure in the form of MnAl6 phase. Manganese can increase the recrystallization temperature of the alloy, prevent the coarsening of crystal grains, and slightly increase the strength of the alloy, especially the yield strength. In high-magnesium aluminum alloys, the addition of manganese can reduce the solubility of magnesium in the matrix, reduce the tendency of weld cracks, and improve the strength of the weld and the base metal. For Price Plz Contact Whatsapp/Wechat: 0086 181 3788 9531 Or Email to nydia@aluminium24.eu

评论

发表评论

此博客中的热门博文

Differences between PS and CTP base plate

图片
With the increasing maturity and the rapid development of CTP technology, as well as the declining of price, CTP technology has been more and more welcomed by the majority of printing practitioners, usage of CTP plates have the potential trend to catch up with the traditional PS plate. The overall requirements of the printing plate is very high, especially the current CTP plate is mostly used for high-grade color printing plate, to ensure the quality of the plate, the plate based apparent quality is the premise. The characteristic of CTP technology is the quality of CTP based plate, such as the apparent quality, physical property and electrolytic performance. The aluminum plate base is widely used according to CTP plate technical requirement. The difference between CTP plates and PS plate on the apparent properties of aluminum plate base are as follows. The basic appearance requirements of the aluminum base plate is clean and smooth, no cracks, corrosion pits, air vents, scratches,...
阅读全文

Mill Finish Aluminum Foil 8011 H14 For Bottle Caps

图片
  Mill finish aluminum foil 8011 H14 for bottle caps has good performance and wide range of applications, usually used to make wine and cosmetic bottle caps. 8011 H14 mill finish aluminum foil for bottle cap material is mainly made of 8011 aluminum alloy, with good corrosion resistance and machinability. H14 temper refers to the hardness state of 8011 aluminum alloy after processing, aluminium foil 8011 h14 has a certain degree of hardness and strength. Mill finish means that the surface of aluminum foil is polished to give it a smooth surface and increase the aesthetic appearance. Mill finish 8011 H14 aluminum foil for bottle cap material has good sealing and freshness preservation properties, and is suitable for all kinds of bottle caps. In the production process, mill finish aluminum foil 8011 H14 for bottle caps material is completed through a number of processes such as cold rolling, foil rolling annealed thickness, annealing, foil rolling finished product, bending and st...
阅读全文

Introduction of aluminum foil insulation material

图片
Aluminum foil insulation material is the best thermal insulation material at present in the world. It has the advantages of light weight, low thermal conductivity, good heat resistance, aging resistance, easy combustion with other substrates, bonding does not produce droplet and other excellent properties. On the application, it is widely used in building roofing, wall, ceiling, floor, doors and windows as insulation materials. Aluminum foil itself is a good conductor of heat, directly used basically has no heat insulation, but accelerate the heat loss, so when used the insulation cotton is wrapped inside the aluminum foil . It has the functions of heat insulation, waterproof, moisture-proof and so on. Its solar radiation absorption coefficient is very low, which can insulate most of the heat transfer. Introduction of advantages of aluminum foil insulation material: (1) Simplification of structure to avoid waste. (2) It is unnecessary to set roof exhaust system. (3) Waterproof lay...
阅读全文